5kgs per bottle, 20kgs per carton
20kgs per barrel
200kgs per barrel
Epoxy resin 312AB-8 can be cured under normal temperature and low temperature, natural defoaming, anti-yellow, high transparency, no ripple, bright in surface, it can be cured faster at high temperature. ..
Properties before Hardening
A: B = 100:33(weight ratio)
25 ℃×8H to 10H or 55℃×1.5H (2 g)
1.Weigh A and B glue according to the given weight ratio into the prepared cleaned container, fully mixed the mixture again the container wall by clockwise, place it along for 3 to 5 minutes, and then it can be used.
2.Take the glue according to the usable time and dosage of mixture to avoid wasting. When the temperature is below 15 ℃, please heat A glue to 30 ℃ first and then mix it to the B glue (A glue will be thicken in low temperature ); The glue must be sealed lid after use to avoid rejection caused by moisture absorption.
3.When the relative humidity is higher than 85%, the surface of the cured mixture will absorb moisture in the air, and form a layer of white mist in the surface, so when the relative humidity is higher than 85%, is not suitable for room temperature curing, suggest to use the heat curing.
Properties after Hardening
Withstand voltage, KV/mm
Flexural strength, Kg/mm2
Volume resistivity, Ohm3
Surface resistance, Ohmm2
Thermal conductivity, W/M.K
Induced electric loss, 1KHZ
Moisture absorption, %
Compressed strength, Kg/ mm2
1,The operating environment should be ventilative and should keep away from fire. Closely sealed after use.
2, Avoid eye contact, in case of contact, wash with plenty of water and get medical attention immediately.
3, If contact skin, wrap with clean cloth or paper, and wash it with water and soap.
4, Keep away from children.
5, Please take a trial before application to avoid usage mistake.